Fiberon™ PA6-CF20 Black – Polymaker

$89.90

Fiberon™ PA6-CF20 is a carbon fibre reinforced PA6 (Nylon 6) filament. The carbon fibre reinforcement provides significantly improved stiffness, strength and heat resistance with outstanding layer adhesion.

0.5kg - Black

In stock (can be backordered)

Fiberon™ PA6-CF20

Exceptional stiffness, strength, heat resistance up to 215°C, with superior layer adhesion!

The PA6-CF20 filament from the Fiberon line of high-performance polymers is a PA6-based material reinforced with 20% carbon fiber, offering exceptional strength, stiffness, and isotropic rigidity. With a heat resistance reaching up to 215 ºC, PA6-CF20 is suitable for demanding applications that require stability under high temperatures. It also features Fiber Adhesion™ Technology, which promotes superior layer adhesion, resulting in robust, cohesive printed parts. These properties make PA6-CF20 ideal for challenging uses in automotive, composite manufacturing, and industrial components, where performance and durability are critical. If a filament with even better mehanical properties and reduced moisture sensitivity is required, please see the Fiberon PA612-CF15 filament.

Printing Requirements

All-metal hotend 280˚C+
Hardened nozzle
Filament dryer
Annealing post printing
Moisture conditioning after Annealing

Specification

TDS Download SDS Download

Download a printer profile

Bambu Lab QIDITECH RAISE3D

Polymaker Fiberon™ PA612-CF15 Black

General information
Material	PA
Format	500 g / 3 kg
Density	(ISO 1183) 1.17 g/cm³
Filament diameter	1.75 mm
Filament length	(Ø 1.75 mm-0.5 Kg) ±177.7 m / (Ø 1.75 mm-3 Kg) ±1066.0 m

Electrical properties
Surface electrical resistivity	(ANSI ESD S11.11) OL, >10¹² Ohm

Printing properties
Printing temperature	280 – 300 ºC
Print bed temperature	40 – 50 ºC
Chamber temperature	20 – 25 ºC
Cooling fan	✗
Recommended printing speed	Max. 300 mm/s
Recommended nozzle	Hardened Steel

Mechanical properties
Charpy impact strength	(ISO 179) 11.0 ± 0.3 KJ/m²
Elongation at break	(ISO 527) XY: 2.1 ± 0.2 % / Z: 1.9 ± 0.4 %
Tensile strength	(ISO 527) XY: 109.3 ± 2.4 MPa / Z: 54.0 ± 5.2 MPa
Tensile modulus	(ISO 527) XY: 8636.5 ± 211.4 MPa / Z: 3759.5 ± 118.5 MPa
Flexural strength	(ISO 306) XY: 161.0 ± 3.9 MPa / Z: – MPa
Flexural modulus	(ISO 178) XY: 7037.6 ± 205.4 MPa / Z: – MPa
Surface hardness	–

Thermal properties
Melting temperature	(DSC) 218.5 ºC
Softening temperature	– ºC
Heat deflexion temperature	(ISO 75) @ 0.45 MPa: 215 ºC / @ 1.8 MPa: 173 ºC

Specific properties
Transparency	✗
Flammability classification	UL 94 HB @ 1.5 mm
Chemical resistance	✓

Weight	0.5 kg
Dimensions	210 × 210 × 50 cm
Brand	Polymaker
Colour	Black