Fiberon™ PA6-CF20 Black – Polymaker
$89.90
Fiberon™ PA6-CF20 is a carbon fibre reinforced PA6 (Nylon 6) filament. The carbon fibre reinforcement provides significantly improved stiffness, strength and heat resistance with outstanding layer adhesion.
0.5kg - Black
In stock (can be backordered)
Fiberon™ PA6-CF20
Exceptional stiffness, strength, heat resistance up to 215°C, with superior layer adhesion!
The PA6-CF20 filament from the Fiberon line of high-performance polymers is a PA6-based material reinforced with 20% carbon fiber, offering exceptional strength, stiffness, and isotropic rigidity. With a heat resistance reaching up to 215 ºC, PA6-CF20 is suitable for demanding applications that require stability under high temperatures. It also features Fiber Adhesion™ Technology, which promotes superior layer adhesion, resulting in robust, cohesive printed parts. These properties make PA6-CF20 ideal for challenging uses in automotive, composite manufacturing, and industrial components, where performance and durability are critical. If a filament with even better mehanical properties and reduced moisture sensitivity is required, please see the Fiberon PA612-CF15 filament.
Printing Requirements
- All-metal hotend 280˚C+
- Hardened nozzle
- Filament dryer
- Annealing post printing
- Moisture conditioning after Annealing
Specification
TDS Download SDS Download
General information | |
| Material | PA |
| Format | 500 g / 3 kg |
| Density | (ISO 1183) 1.17 g/cm³ |
| Filament diameter | 1.75 mm |
| Filament length | (Ø 1.75 mm-0.5 Kg) ±177.7 m / (Ø 1.75 mm-3 Kg) ±1066.0 m |
Electrical properties | |
| Surface electrical resistivity | (ANSI ESD S11.11) OL, >10¹² Ohm |
Printing properties | |
| Printing temperature | 280 – 300 ºC |
| Print bed temperature | 40 – 50 ºC |
| Chamber temperature | 20 – 25 ºC |
| Cooling fan | ✗ |
| Recommended printing speed | Max. 300 mm/s |
| Recommended nozzle | Hardened Steel |
Mechanical properties | |
| Charpy impact strength | (ISO 179) 11.0 ± 0.3 KJ/m² |
| Elongation at break | (ISO 527) XY: 2.1 ± 0.2 % / Z: 1.9 ± 0.4 % |
| Tensile strength | (ISO 527) XY: 109.3 ± 2.4 MPa / Z: 54.0 ± 5.2 MPa |
| Tensile modulus | (ISO 527) XY: 8636.5 ± 211.4 MPa / Z: 3759.5 ± 118.5 MPa |
| Flexural strength | (ISO 306) XY: 161.0 ± 3.9 MPa / Z: – MPa |
| Flexural modulus | (ISO 178) XY: 7037.6 ± 205.4 MPa / Z: – MPa |
| Surface hardness | – |
Thermal properties | |
| Melting temperature | (DSC) 218.5 ºC |
| Softening temperature | – ºC |
| Heat deflexion temperature | (ISO 75) @ 0.45 MPa: 215 ºC / @ 1.8 MPa: 173 ºC |
Specific properties | |
| Transparency | ✗ |
| Flammability classification | UL 94 HB @ 1.5 mm |
| Chemical resistance | ✓ |
| Weight | 0.5 kg |
|---|---|
| Dimensions | 210 × 210 × 50 cm |
| Brand | |
| Colour | Black |
Related products
Add to cart DetailsBuy Now1kg high quality premium and well priced 1.75mm PLA Pro 3D Printer composite CF filament. It was engineered, similar to other PLA+ materials, for better printing performance. 15% CF
- Add to cart DetailsBuy Now
Proto-pasta Carbon Fibre Composite is a combination of milled carbon Fibres and high-performance PLA. Resulting 3D prints made with our Carbon Fibre HTPLA are demonstrably more rigid, providing excellent structural strength and layer adhesion with very low warpage.
- Add to cart DetailsBuy Now
PA100 Nylon-Like Resin is a high-strength resin material developed by eSUN for engineering and manufacturing. It has good toughness, impact resistance, good durability, low shrinkage and high precision, and is widely compatible with color screen and mono-screen printers. As an engineering-grade resin material, it can be used to make models or components such as fixtures, stencils, aircraft models, industrial parts, samples, joints, snaps, gears, etc.
- Add to cart DetailsBuy Now
Polymaker PolyMide™ CoPA is based on a copolymer of Nylon 6 and Nylon 6,6. The filament combines excellent strength, toughness, and heat resistance of up to 180˚C.
Reviews
There are no reviews yet.